Structure, Morphology, and Surface Chemistry of Surgical Masks and Their Evolution up to 10 Washing Cycles

Joseph Garnier
Lara Leclerc
Paul O Verhoeven

Résumé

The Covid-19 crisis has led to a massive surge in the use of surgical masks worldwide, causing risks of shortages and high pollution. Various decontamination techniques are currently being studied to reduce these risks by allowing the reuse of masks. In this study, surgical masks were washed up to 10 times, each cycle under the same conditions. The consequences of the washing cycles on the structure, fiber morphology, and surface chemistry have been studied through several characterization techniques: scanning electron microscopy, wetting angle measurements, infrared spectroscopy, X-ray diffraction, and X-ray photoelectrons spectroscopy. The washing process did not induce large changes in the hydrophobicity of the surface, the contact angle remaining constant throughout the cycles. The composition observed in the IR spectrum also remained unchanged for washed masks up to 10 cycles. Some slight variations were observed during X-ray analysis: the crystallinity of the fibers as well as the size of the crystals increases with the number of wash cycles. The XPS analysis shows that after 10 cycles, the surface of the masks underwent a slight oxidation. In the SEM images, changes were observed in the arrangement of the fibers, which are more visible the more times the mask has been washed: they align themselves in bundles, form areas with holes in the mask layer, and are crushed in some areas.

Domaines

Polymères
Fichier principal
Vignette du fichier
2023 Wittmann - ACS Applied Polymer Materials.pdf (4.59 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04106860 , version 1 (26-05-2023)

Licence

Paternité

Identifiants

Citer

Louise Wittmann, Joseph Garnier, Naomi Sakata, Elisabeth Auzias, Martin Dumoulin, et al.. Structure, Morphology, and Surface Chemistry of Surgical Masks and Their Evolution up to 10 Washing Cycles. ACS Applied Polymer Materials, 2023, 5 (3), pp.2282-2288. ⟨10.1021/acsapm.3c00145⟩. ⟨hal-04106860⟩
41 Consultations
11 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More